Semiconductor substrate, semiconductor device, and manufacturing methods thereof

ABSTRACT

A method of manufacturing a semiconductor substrate includes forming a first semiconductor layer on a substrate, forming a metallic material layer on the first semiconductor layer, forming a first portion of a second semiconductor layer on the first semiconductor layer and the metallic material layer, removing the metallic material layer under the first portion of the second semiconductor layer by dipping the substrate in a solution, forming a second portion of the second semiconductor layer on the first portion of the second semiconductor layer, and forming a cavity in a portion of the first semiconductor layer located under where the metallic material layer was removed.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a divisional of U.S. application Ser. No. 12/801,455, filed on Jun. 9, 2010, and claims priority from and the benefit of Japanese Patent Application No. 2009-139212, filed on Jun. 10, 2009, Japanese Patent Application No. 2009-166682, filed on Jul. 15, 2009, and Japanese Patent Application No. 2009-194334, filed on Aug. 25, 2009, which are hereby incorporated by reference for all purposes as if fully set forth herein.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present disclosure relates to semiconductor substrates, semiconductor devices, and manufacturing methods thereof. More particularly, the present disclosure relates to semiconductor substrates having a GaN layer formed on a substrate, semiconductor devices, and manufacturing methods thereof.

2. Discussion of the Background

A light emitting diode (LED) that has a gallium nitride (GaN) based semiconductor may be used for various applications, such as signal devices, backlight units for liquid crystal panels, and the like. It is known that light emitting efficiency of LEDs is affected by dislocation density and defects in a crystal. Although GaN-based semiconductor crystals may be grown on a heterogeneous substrate, such as sapphire or the like, lattice mismatch and differences in thermal expansion between the GaN layer and the substrate may occur, causing a high dislocation density or an increase in defect density.

The crystal growth of a GaN-based semiconductor may be carried out on a homogeneous substrate, such as a GaN substrate and the like. However, a high dissociation rate of nitrogen in GaN may obstruct formation of a GaN melt, thereby making it difficult to form a GaN substrate. Although mechanical polishing, laser delamination or the like may be used to separate the GaN substrate from a GaN bulk crystal grown for the GaN substrate, it may be difficult to produce a GaN substrate having a practical size. Particularly, the laser delamination may require a significantly long period of time to perform and cause an increase in the cost of the GaN substrate.

GaN crystal growth is shown and described in “Polycrystalline GaN for light emitter and field electron emitter applications,” by S. Hasegawa, S. Nishida, T. Yamashita, H. Asahi, (Thin Solid Films 487 (2005), pp 260-267) (hereinafter “Hasegawa, et al.”), and “Buried Tungsten Metal Structure Fabricated by Epitaxial-Lateral-Overgrown GaN via Low-Pressure Metalorganic Vapor Phase Epitaxy,” M. Haino, et al., (Jpn. J. Appl. Phys., 39 (2000) L449) (hereinafter “Haino, et. al.”), which are hereby incorporated by reference in their entirety for all purposes as if fully set forth herein. For example, GaN crystals are respectively grown on quartz substrates, high-melting-point metal substrates of Tungsten (W), Molybdenum (Mo), Tantalum (Ta), and Niobium (Nb), and Silicon (Si) substrates using plasma assisted molecular beam epitaxy.

Since it may be difficult and costly to fabricate the GaN substrate, semiconductor devices such as LEDs or laser diodes are generally manufactured by growing a GaN layer on a heterogeneous substrate, such as sapphire and the like. However, as mentioned above, the high dislocation density or the increase in defect density may degrade the light emitting efficiency of the LED. In addition, the sapphire substrate has a lower thermal conductivity than the GaN substrate, and may cause deterioration in heat dissipation properties of a device. Thus, the use of a sapphire substrate for LEDs or laser diodes may limit the operational lifespan thereof.

SUMMARY OF THE INVENTION

The present invention provides a method of manufacturing a flat and easily separable GaN substrate on a heterogeneous substrate at low cost.

The present invention also provides a semiconductor device manufactured using the GaN substrate which may have improved performance or long operational lifespan.

Additional features of the invention will be set forth in the description which follows, and in part will be apparent from the description, or may be learned by practice of the invention.

The present invention discloses a semiconductor substrate including a substrate, a first semiconductor layer arranged on the substrate; a metallic material layer arranged on the first semiconductor layer, a second semiconductor layer arranged on the first semiconductor layer and the metallic material layer, and a cavity formed at a portion of the first semiconductor layer under the metallic material layer.

The present invention also discloses a semiconductor substrate including a substrate, a first semiconductor layer arranged on the substrate, a second semiconductor layer arranged on the first semiconductor layer, and a cavity formed in the first semiconductor layer.

The present invention also discloses a method of manufacturing a semiconductor substrate including forming a first semiconductor layer on a substrate, forming a metallic material layer on the first semiconductor layer, forming a second semiconductor layer on the first semiconductor layer and the metallic material layer, and forming a cavity in a portion of the first semiconductor layer under the metallic material layer.

The present invention also discloses a method of manufacturing a semiconductor substrate including forming a first semiconductor layer on a substrate, forming a metallic material layer on the first semiconductor layer, forming a first portion of a second semiconductor layer on the first semiconductor layer and the metallic material layer, removing the metallic material layer under the first portion of the second semiconductor layer by dipping the substrate in a solution, forming a second portion of the second semiconductor layer on the first portion of the second semiconductor layer, and forming a cavity in a portion of the first semiconductor layer located under where the metallic material layer was removed.

It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory and are intended to provide further explanation of the invention as claimed.

BRIEF DESCRIPTION OF THE DRAWINGS

The patent or application file contains at least one drawing executed in color. Copies of this patent or patent application publication with color drawings will be provided by the Office upon request and payment of the necessary fee.

The accompanying drawings, which are included to provide a further understanding of the invention and are incorporated in and constitute a part of this specification, illustrate embodiments of the invention, and together with the description serve to explain the principles of the invention.

FIG. 1 is a flow diagram of a method of manufacturing a semiconductor substrate in accordance with a first exemplary embodiment of the present invention, in which (A) is a sectional view of a process of forming a first GaN layer, (B) is a sectional view of a process of forming a Ta layer, (C) is a sectional view of a process of forming a second GaN layer and a cavity, (D) is a sectional view of the semiconductor substrate after forming the second GaN layer, (E) is a sectional view of the semiconductor substrate from which a sapphire substrate is separated, and (F) is a sectional view of a finished GaN substrate.

FIG. 2 is a scanning electron microscope (SEM) image of a semiconductor substrate of a first example of the first exemplary embodiment.

FIG. 3 is an energy dispersive x-ray spectrometer (EDX) spectrum of the semiconductor substrate of the first example of the first exemplary embodiment.

FIG. 4 is a SEM micrograph and EDX diagrams of the semiconductor substrate according to the first example of the first exemplary embodiment, in which (A) is a SEM micrograph of an enlarged region shown in FIG. 2, (B) is an EDX diagram of Ga, (C) is an EDX diagram of Al, and (D) is an EDX diagram of O.

FIG. 5 is SEM micrographs of the semiconductor substrate according to the first example of the first exemplary embodiment, in which (A) is a SEM micrograph of a side section of the semiconductor substrate and (B) is a SEM micrograph of a surface of the semiconductor substrate.

FIG. 6 is EDX diagrams of the semiconductor substrate according to the first example of the first exemplary embodiment, in which (A) is an EDX diagram of Ga and (B) is an EDX diagram of Ta.

FIG. 7 is SEM micrographs of a semiconductor substrate according to a first comparative example, in which (A) is a SEM micrograph of the semiconductor substrate and (B) is a SEM micrograph of a surface of the semiconductor substrate.

FIG. 8 is an EDX spectrum and EDX diagrams of the semiconductor substrate according to the first comparative example, in which (A) is an EDX spectrum of the semiconductor substrate of FIG. 7(B), (B) is an EDX diagram of Ga of FIGS. 7(B), and (C) is an EDX diagram of N of FIG. 7(B).

FIG. 9 is a SEM micrograph and an EDX spectrum of the semiconductor substrate according to the first comparative example, in which (A) is a SEM micrograph of a side section of a void and (B) is an EDX spectrum of the void of FIG. 9(A).

FIG. 10 is EDX diagrams of the semiconductor substrate according to the first comparative example, in which (A) is an EDX diagram of Ga of FIG. 9(A), (B) is an EDX diagram of N of FIGS. 9(A), and (C) is an EDX diagram of Ta of FIG. 9(A).

FIG. 11 is a sectional view of an LED array in accordance with a fourth exemplary embodiment of the present invention.

FIG. 12 is a SEM micrograph of a side section of a semiconductor substrate according to a second example of the first exemplary embodiment.

FIG. 13 is a SEM micrograph of a side section of a semiconductor substrate of according to a third example of the first exemplary embodiment.

FIG. 14 is a SEM micrograph of a side section of a semiconductor substrate of according to a fourth example of the first exemplary embodiment.

FIG. 15(A) is a diagram showing an exemplary embodiment of a Ta2O5 film converted from a 5 nm thick Ta layer, and FIG. 15(B) is a diagram showing an exemplary embodiment of a Ta2O5 film formed on a surface of a 100 nm thick Ta layer.

FIG. 16(A) is a SEM micrograph of a surface of a substrate having a 5 nm thick Ta mask, and FIG. 16(B) is a SEM micrograph of a surface of a substrate having a 10 nm thick Ta2O5 mask.

FIG. 17 is a flow diagram of a method of manufacturing a semiconductor substrate in accordance with a second exemplary embodiment, in which (A) is a sectional view of a process of forming a first GaN layer, (B) is a sectional view of a process of forming a Ta layer, (C) is a sectional view of a process of forming a second GaN layer and a cavity, (D) is a sectional view of the semiconductor substrate after forming the second GaN layer, (E) is a sectional view of the semiconductor substrate from which a sapphire substrate is separated, and (F) is a sectional view of a finished GaN substrate.

FIG. 18(A) is a SEM micrograph of a side section of a semiconductor substrate according to a first example of the second exemplary embodiment, and FIG. 18(B) is a SEM micrograph of a side section of the semiconductor substrate of a first comparative example.

FIG. 19(A) is a SEM micrograph of a side section of a semiconductor substrate according to a second example of the second exemplary embodiment formed in a first condition and FIG. 19(B) is a SEM micrograph of a side section of a semiconductor substrate according to a second example of the second exemplary embodiment formed in a second condition.

FIG. 20 is a SEM micrograph of a side section of a semiconductor substrate formed using a tungsten (W) layer according to a second comparative example.

FIG. 21 is a SEM micrograph of a side section of a semiconductor substrate formed using a plutonium (Pt) layer according to a second comparative example.

FIG. 22 is a SEM micrograph of a side section of a semiconductor substrate formed using a nickel (Ni) layer according to a second comparative example.

FIG. 23 is a SEM micrograph of a side section of a semiconductor substrate formed using a molybdenum (Mo) layer according to a second comparative example.

FIG. 24A is a flow diagram of a method of manufacturing a semiconductor substrate in accordance with a third exemplary embodiment, in which (A) is a sectional view of a process of forming a first GaN layer, (B) is a sectional view of a process of forming a Ta layer, (C) is a sectional view of a process of forming a second GaN layer and a cavity, (D) is a sectional view of the second GaN layer after removing the Ta layer by ultrasound cleaning, and (E) is a sectional view of a finished second GaN substrate.

FIG. 24B is a flow diagram of a method of manufacturing a semiconductor substrate in accordance with a third exemplary embodiment, in which (A) is a sectional view of a process of forming a first GaN layer, (B) is a sectional view of a process of forming a Ta layer, (C) is a sectional view of a process of forming a second GaN layer and a cavity, (D) is a sectional view of the second GaN layer after removing the Ta layer by ultrasound cleaning, and (E) is a sectional view of a finished third GaN substrate.

FIG. 25A is a flow diagram of the method of manufacturing a semiconductor substrate in accordance with the third exemplary embodiment continuing from FIG. 24A, in which (A) is a sectional view of the semiconductor substrate from which the sapphire substrate is separated and (B) is a sectional view of a finished GaN substrate.

FIG. 25B is a flow diagram of the method of manufacturing a semiconductor substrate in accordance with the third exemplary embodiment continuing from FIG. 24B, in which (A) is a sectional view of the semiconductor substrate from which the sapphire substrate is separated and (B) is a sectional view of a finished GaN substrate.

FIG. 26(A) is a SEM micrograph of a surface of a semiconductor substrate having a portion of a second GaN layer formed by the method in accordance with the third exemplary embodiment, and FIG. 26(B) is a SEM micrograph of a side section of the semiconductor substrate of FIG. 26(A).

FIG. 27(A) is an optical micrograph of a surface of a semiconductor substrate formed by the method in accordance with the third exemplary embodiment, from which the Ta layer is removed, and FIG. 26(B) is a SEM micrograph of a side section of the semiconductor substrate of FIG. 27(A), on which the second GaN layer is formed.

FIG. 28 is sectional views of the semiconductor substrate formed by the method in accordance with the third exemplary embodiment, showing a grown state of a GaN layer, in which (A) shows first GaN layers separated a narrow distance from each other, and (B) shows first GaN layers separated a wide distance from each other.

FIG. 29 is sectional views of the semiconductor substrate formed by the method in accordance with the third exemplary embodiment, in which (A) shows TMG density and a grown state of the GaN layer when the first GaN layers are separated a narrow distance from each other and an internal pressure of an MOCVD apparatus is low, (B) shows TMG density and a grown state of the GaN layer when the first GaN layers are separated a wide distance from each other and the internal pressure of the MOCVD apparatus is high, (C) shows TMG density and a grown state of the GaN layer when the first GaN layers are separated a narrow distance from each other and the internal pressure of the MOCVD apparatus is high, and (D) shows TMG density and a grown state of the GaN layer when the first GaN layers are separated a wide distance from each other and the internal pressure of the MOCVD apparatus is low.

DETAILED DESCRIPTION OF THE ILLUSTRATED EMBODIMENTS

The invention is described more fully hereinafter with reference to the accompanying drawings, in which exemplary embodiments of the invention are shown. This invention may, however, be embodied in many different forms and should not be construed as limited to the exemplary embodiments set forth herein. Rather, these exemplary embodiments are provided so that this disclosure is thorough, and will fully convey the scope of the invention to those skilled in the art. In the drawings, the size and relative sizes of layers and regions may be exaggerated for clarity. Like reference numerals in the drawings denote like elements.

It will be understood that when an element such as a layer, film, region or substrate is referred to as being “on” another element, it can be directly on the other element or intervening elements may also be present. In contrast, when an element is referred to as being “directly on” another element, there are no intervening elements present.

FIG. 1 is a flow diagram of a method of manufacturing a semiconductor substrate 100 in accordance with a first exemplary embodiment. In FIG. 1, (A) is a sectional view of a process of forming a first GaN layer, (B) is a sectional view of a process of forming a Ta layer, (C) is a sectional view of a process of forming a second GaN layer and a cavity, (D) is a sectional view of the semiconductor substrate after forming the second GaN layer, (E) is a sectional view of the semiconductor substrate from which a sapphire substrate is separated, and (F) is a sectional view of a finished GaN substrate.

Referring to FIG. 1(A), reference numeral 101 indicates a sapphire (Al2O3) substrate. First, a first GaN layer 102 having a thickness of about 2 μm is formed on the sapphire substrate 101. This thickness of the first GaN layer 102 is provided as an example.

Next, referring to FIG. 1(B), a Ta layer (metallic material layer) 103 having a thickness of about 50 nm is formed in a shape of stripes, which have a width of 5 μm and are separated a distance of 5 μm from each other, on the first GaN layer 102 by electron beam (EB) deposition and lift-off. The shape, thickness, width, distance of the Ta layer 103 are provided as an example.

Referring to FIG. 1(C), a second GaN layer 104 is formed on the first GaN layer 102 and the Ta layer 103 by metal organic chemical vapor deposition (MOCVD). The first GaN layer 102 and the second GaN layer 104 may include different semiconductor material such as AlGaN, InGaN, or AlInGaN. FIG. 1(C) shows the second GaN layer 104 during formation thereof. In the present exemplary embodiment, N in the first GaN layer 102 combine with Ta to form TaN, which acts as foreign matter and rises towards a vapor having a higher density of N. The TaN becomes unstable at 900° C. or more, and a hole 103 a is deepened to form a cavity 102 a depending on the degree of instability. Here, although N in the first GaN layer 102 becomes TaN, Ga remains in the first GaN layer 102. Since this Ga remaining in the first GaN layer 102 is the same as Ga deposited during the vapor deposition, it is used as the raw material. However, GaN may also be grown on a Ta film. As disclosed in Hasegawa, et al., there is a possibility that the surface of the Ta layer 103 becomes not only Ta, but also Ta2O5 in a reaction with air.

Next, referring to FIG. 1(D), once the formation of the second GaN layer 104 is completed, the semiconductor substrate 100 is formed. While the second GaN layer 104 is formed by MOCVD, a portion of the first GaN layer 102 under the Ta layer 103 is removed by etching and a formation region of the cavity 102 a is extended substantially to the sapphire substrate 101. Further, the surface of the substrate is flattened to progress the growth of the first GaN layer 102 along with the growth of the second GaN layer 104, as shown in FIG. 1.

Next, referring to FIG. 1(E), the sapphire substrate 101 is separated from the first GaN layer 102. Then, referring to FIG. 1(F), the GaN substrate 100 may be obtained by polishing the first GaN layer 102, from which the sapphire substrate is removed. The GaN substrate 100 may be used as a semiconductor substrate for manufacturing a device by attaching a silicon-based substrate such as Si or SiC to an upper side of the GaN substrate 100 and flattening a lower surface thereof. Furthermore, the cavity 102 a formed in the first GaN layer 102 may be used to separate the sapphire substrate 101. Separation of the sapphire substrate 101 may also be performed by, for example, a laser lift-off or polishing process. The sapphire substrate 101 may be separated from the first GaN layer 102 using any suitable method.

As such, when the semiconductor substrate 100 including the GaN layer is formed by MOCVD, the first GaN layer 102 can be easily separated from the sapphire substrate 101 using the cavity 102 a, so that the separated GaN layer can be used as the GaN substrate. Accordingly, the GaN substrate may be manufactured at lower costs than the conventional GaN substrate.

Detailed examples of the manufacturing method of the semiconductor substrate 100 will be described hereinafter. In a first example of the first exemplary embodiment, the process of forming the second GaN layer 104 using an MOCVD apparatus will be described. In this example, crystal growth was performed at a heating temperature of 1045° C. for 5 hours while supplying tri-methyl gallium (TMG) as a raw gas at a flux of 20 μmol/min. Further, in the first example, a Ta layer 103 having a thickness of 50 nm was formed in a shape of stripes on the first GaN layer 102.

In FIG. 2, the semiconductor substrate 100 with the second GaN layer 104 formed thereon under these conditions is shown. FIG. 2 is a SEM micrograph of a side section of a portion of the semiconductor substrate 100. As shown in FIG. 2, the cavity 102 a is formed at a portion of the first GaN layer 102 under the Ta layer 103. An enlarged region including the cavity 102 a in FIG. 2 was analyzed using an energy dispersion x-ray spectrometer (EDX), and the analysis result is shown in FIG. 3.

In the EDX spectrum of FIG. 3, GaN of the first GaN layer 102, and Al and O of the sapphire substrate 101 are observed, but Ta is substantially not observed. Further, in EDX diagrams of FIG. 4(B), FIG. 4(C), and FIG. 4(D), Ga of the first GaN layer 102, and Al and O of the sapphire substrate 101 are observed, but Ta is not substantially observed.

In the first example, it was observed that a hole 103 a was formed in the Ta layer 103 during the formation of the second GaN layer 104. Analysis results of the hole 103 a formed in the Ta layer 103 are shown in FIG. 5 and FIG. 6, and will be described in detail hereinafter. Here, the analysis results shown in FIG. 5 and FIG. 6 were obtained using the EDX by stopping the process of forming the second GaN layer 104 using the MOCVD apparatus.

FIG. 5 shows SEM micrographs of the semiconductor substrate of the first example, in which (A) is a SEM micrograph of a side section of the semiconductor substrate 100 and (B) is a SEM micrograph of a surface of the semiconductor substrate 100. FIG. 6 shows EDX diagrams of the surface of the semiconductor substrate 100 of FIG. 5(B), in which (A) is an EDX diagram of Ga and (B) is an EDX diagram of Ta.

In the SEM micrograph of the semiconductor substrate 100 of FIG. 5(A), it is observed that a portion of the first GaN layer 102 under the Ta layer 103 is etched and the cavity 102 a is formed therein. In the SEM micrograph of the semiconductor substrate 100 of FIG. 5(B), it is observed that holes 103 a were formed on a surface of the Ta layer 103. EDX analysis results for Ga and Ta on the surface of the Ta layer 103 including the holes 103 a are shown in FIG. 6(A) and FIG. 6(B). As shown in the EDX diagrams, the Ta layer 103 remains, and Ga and GaN are thinly grown on the remaining Ta layer 103.

As such, for the semiconductor substrate 100 of the first example, the conditions for forming the second GaN layer 104 using the MOCVD apparatus were adjusted, thereby enabling the cavity 102 a to be formed in the first GaN layer 102 using the Ta layer by etching. Thus, when the second GaN layer 104 was formed as illustrated in the first exemplary embodiment, it was possible to form the cavity 102 a in the first GaN layer 102 by etching during growth of the first GaN layer 102. In other words, when a metallic material layer was partially formed on the first GaN layer 102, it was possible to form the cavity 102 a in the first GaN layer 102. The metallic material layer may be used for etching the first GaN layer 102 as discussed above in relation to the first exemplary embodiment.

In addition, the MOCVD conditions for the first example are provided as an example, and thus, may be set to allow the growth of the first GaN layer and the formation of the cavity 102 a to be simultaneously progressed. Here, since the growth rate of the first GaN layer 102 is slower than that of the second GaN layer 104, the MOCVD conditions were adjusted in consideration of the growth rate of the first GaN layer 102 in the first example.

Further, in the first example, the holes 103 a were formed in the Ta layer 103 during the process of growing the second GaN layer 104, but, for example, the Ta layer 103 may be formed using a mask which is previously formed with a hole. Further, the shape of the Ta layer 103 is not limited to the aforementioned stripe shape, and may be changed depending on a device structure to be formed on the semiconductor substrate 100. An example of a device formed using the semiconductor substrate 100 will be described below.

Further, the semiconductor substrate 100 of the first example may be reused as a substrate 101 forming a GaN layer having the aforementioned cavity by separating the GaN substrate and then a surface of the sapphire substrate 101 on which a new GaN substrate is formed may be flattened by reactive ion etching (RIE) or the like. Hence, manufacturing costs of the GaN substrate can be further reduced.

In a second example of the first exemplary embodiment, the process of forming the second GaN layer 104 using an MOCVD apparatus will be described. In this example, crystal growth was performed at a heating temperature of 1045° C. for 5 hours while supplying TMG as a raw gas at a flux of 20 μmol/min. Further, in the second example, a Ta layer 103 having a thickness of 30 nm was formed in a shape of stripes on the first GaN layer 102.

In FIG. 12, the semiconductor substrate 100 with the second GaN layer 104 formed thereon under these conditions is shown. FIG. 12 is a SEM micrograph of a side section of a portion of the semiconductor substrate 100. As shown in this figure, a cavity 102 a is formed at a portion of the first GaN layer 102 under the Ta layer 103. Further, in the second example, it was observed that a hole 103 a was formed in the Ta layer 103 during the formation of the second GaN layer 104.

For the semiconductor substrate 100 of the second example, the conditions for forming the second GaN layer 104 using the MOCVD apparatus were adjusted, thereby enabling the cavity 102 a to be formed in the first GaN layer 102 using the Ta layer 103 by etching. Thus, when the second GaN layer 104 is formed as illustrated in the second example, it is possible to form the cavity 102 a in the first GaN layer 102 by etching during growth of the first GaN layer 102. In other words, when a metallic material layer was partially formed on the first GaN layer 102 it was possible to form the cavity 102 a in the first GaN layer 102. The metallic material layer may be used for the etching the first GaN layer 102 as discussed above in relation to the first exemplary embodiment.

In the sectional view of FIG. 12, the cavities 102 a caused by etching are not formed in the first GaN layer 102 under the overall lower surface of each of the Ta layers 103, but under opposite ends of each of the Ta layers 103. FIG. 12 shows that etching is performed in the first GaN layer 102 from the opposite ends of each of the Ta layers 103.

Further, the MOCVD conditions for the second example are provided as an example, and thus, may be set to allow the growth of the first GaN layer and the formation of the cavity 102 a to be simultaneously progressed. Here, since the growth rate of the first GaN layer 102 is slower than that of the second GaN layer 104, the MOCVD conditions were adjusted in consideration of the growth rate of the first GaN layer 102 in the second example.

Further, in the second example, the holes 103 a were formed in the Ta layer 103 during the process of growing the second GaN layer 104, but, for example, the Ta layer 103 may be formed using a mask which is previously formed with a hole. Further, the shape of the Ta layer 103 is not limited to the aforementioned stripe shape, and may be changed depending on a device structure to be formed on the semiconductor substrate 100. An example of a device formed using the semiconductor substrate 100 will be described below.

Further, the semiconductor substrate 100 of the second example may be reused as a substrate 101 for forming a GaN layer having the aforementioned cavity. The GaN substrate may be separated and then a surface of the sapphire substrate 101 on which a new GaN substrate is formed may be flattened by RIE or the like. Hence, manufacturing costs of the GaN substrate can be further reduced.

In a third example of the first exemplary embodiment, the process of forming the second GaN layer 104 using an MOCVD apparatus will be described. In this example, crystal growth was performed at a heating temperature of 1045° C. for 5 hours while supplying TMG as a raw gas at a flux of 20 μmol/min. Further, in the third example, a Ta layer 103 having a thickness of 50 nm was formed in a shape of stripes on the first GaN layer 102.

In FIG. 13, the semiconductor substrate 100 with the second GaN layer 104 formed thereon under these conditions is shown. FIG. 13 is an SEM micrograph of a side section of a portion of the semiconductor substrate 100. As shown this figure, a cavity 102 a is formed at a portion of the first GaN layer 102 under the Ta layer 103. Further, in the third example, it was observed that holes 103 a were formed in the Ta layer 103 during the formation of the second GaN layer 104.

For the semiconductor substrate 100 of the third example, the conditions for forming the second GaN layer 104 using the MOCVD apparatus were adjusted, thereby enabling the cavity 102 a to be formed in the first GaN layer 102 under the Ta layer 103 by etching. Thus, when the second GaN layer 104 was formed as illustrated in the first exemplary embodiment, it was possible to form the cavity 102 a in the first GaN layer 102 by etching during growth of the first GaN layer 102. In other words, when a metallic material layer was partially formed on the first GaN layer 102 it was possible to form the cavity 102 a in the first GaN layer 102. The metallic material layer may be used for etching the first GaN layer 102 as discussed above in relation to the first exemplary embodiment.

In addition, the MOCVD conditions for the third example are provided as an example, and thus, may be set to allow the growth of the first GaN layer 102 and the formation of the cavity 102 a to be simultaneously progressed. Here, since the growth rate of the first GaN layer 102 is slower than that of the second GaN layer 104, the MOCVD conditions were adjusted in consideration of the growth rate of the first GaN layer 102 in the third example.

Further, in the third example, the holes 103 a were formed in the Ta layer 103 during the process of growing the second GaN layer 104, but the Ta layer 103 may be formed using a mask which is previously formed with a hole. Further, the shape of the Ta layer 103 is not limited to the aforementioned stripe shape, and may be changed depending on a device structure to be formed on the semiconductor substrate 100. An example of a device formed using the semiconductor substrate 100 will be described below.

Further, the semiconductor substrate 100 of the third example may be reused as a substrate 101 for forming a GaN layer having the aforementioned cavity. The GaN substrate may be separated and then a surface of the sapphire substrate 101 on which a new GaN substrate is formed may be flattened by RIE or the like. Hence, manufacturing costs of the GaN substrate can be further reduced.

In a fourth example of the first exemplary embodiment, the process of forming the second GaN layer 104 using an MOCVD apparatus will be described. In this example, crystal growth was performed at a heating temperature of 1045° C. for 5 hours while supplying TMG as a raw gas at a flux of 20 μmol/min. Further, in the fourth example, a Ta layer 103 having a thickness of 100 nm was formed in a shape of stripes on the first GaN layer 102.

In FIG. 14, the semiconductor substrate 100 with the second GaN layer 104 formed thereon under these conditions is shown. FIG. 14 is a SEM micrograph of a side section of a portion of the semiconductor substrate 100. As shown this figure, a cavity 102 a is formed at a portion of the first GaN layer 102 under the Ta layer 103. Further, in the fourth example, it was observed that holes 103 a were formed in the Ta layer 103 during the formation of the second GaN layer 104.

For the semiconductor substrate 100 of the fourth example, the conditions for forming the second GaN layer 104 using the MOCVD apparatus were adjusted, thereby enabling the cavity 102 a to be formed in the first GaN layer 102 using the Ta layer 103 by etching. Thus, when the second GaN layer 104 was formed as illustrated in the first exemplary embodiment, it was possible to form the cavity 102 a in the first GaN layer 102 by etching during growth of the first GaN layer 102. In other words, when a metallic material layer was partially formed on the first GaN layer 102 it was possible to form the cavity 102 a in the first GaN layer 102. The metallic material layer may be used for etching the first GaN layer 102 as discussed above in relation to the first exemplary embodiment.

In addition, the MOCVD conditions for the fourth example are provided as an example, and thus, may be set to allow the growth of the first GaN layer and the formation of the cavity 102 a to be simultaneously progressed. Here, since the growth rate of the first GaN layer 102 is slower than that of the second GaN layer 104, the MOCVD conditions were adjusted in consideration of the growth rate of the first GaN layer 102 in the fourth example.

Further, in the fourth example, the holes 103 a were formed in the Ta layer 103 during the process of growing the second GaN layer 104, but, for example, the Ta layer 103 may be formed using a mask which is previously formed with a hole. Further, the shape of the Ta layer 103 is not limited to the aforementioned stripe shape, and may be changed depending on a device structure to be formed on the semiconductor substrate 100. An example of a device formed using the semiconductor substrate 100 will be described below.

Further, the semiconductor substrate 100 of the fourth example may be reused as a substrate 101 for forming a GaN layer having the aforementioned cavity. The GaN substrate may be separated and a surface of the sapphire substrate 101 on which a new GaN substrate is formed may be flattened by RIE or the like. Hence, manufacturing costs of the GaN substrate can be further reduced.

A first comparative example will be described hereinafter. In the first comparative example, the process of forming the second GaN layer 104 of the semiconductor substrate 100 with a different condition of the MOCVD apparatus will be described.

In the first comparative example, crystal growth was performed at a heating temperature of 1045° C. for 5 hours while supplying TMG as a raw gas at a flux of 87 μmol/min.

In FIG. 7, the semiconductor substrate 100 with the second GaN layer 104 formed thereon under these conditions is shown. In FIG. 7, (A) is a SEM micrograph of a side section of a portion of the semiconductor substrate 100 and (B) is a SEM micrograph of a surface of the semiconductor substrate shown in (A). As shown in these micrographs, granular materials are precipitated on the surface of the second GaN layer 104 and a cavity 102 a is formed at a portion of the first GaN layer 102 under the Ta layer 103. The following EDX analysis shows that the granular materials are Ga granules, N granules, and Ta granules.

FIG. 8 shows results of EDX analysis on the surface of the granular materials, in which (A) is an EDX spectrum of the granular materials shown in FIG. 7(B), (B) is an EDX diagram of Ga obtained by EDX analysis of the granular materials of FIG. 7(B), and (C) is an EDX diagram of N obtained by EDX analysis of the granular materials of FIG. 7(B). In the EDX spectrum of FIG. 8(A), Ga, N and a trace of Ta are observed, so that Ga and N are observed as shown in the EDX diagrams of FIG. 8(B) and FIG. 8(C).

Results of EDX analysis on cross sections of the granular materials are shown in FIGS. 9 and 10. In FIG. 9, (A) is a SEM micrograph of a side section of a void formed as a granular material shown in FIG. 7(B) and (B) is an EDX spectrum of the void shown in (A). In FIG. 10, (A) is an EDX diagram of Ga obtained by EDX analysis on the side section of the void of FIG. 9(A), (B) is an EDX diagram of N obtained by EDX analysis on the side section of the void of FIG. 9(A), and (C) is an EDX diagram of Ta obtained by EDX analysis on the side section of the void of FIG. 9(A).

In the spectrum of FIG. 9(B), Ga and N of the second GaN layer 104 and the granular materials, Ta of the Ta layer 103, and Al and O of the sapphire substrate 101 are observed. Further, as shown in (A) to (C) of FIG. 10, Ga, N and Ta are observed at the void.

The granular materials precipitated on the surface of the second GaN layer 104 are Ga granules, N granules, and Ta granules.

Formation of Ta2O5 region in Ta layer

In the first, second, third, and fourth examples, the thickness of the Ta layer 103 was changed to 30 nm, 50 nm, and 100 nm. It could be ascertained that the cavity 102 a was formed in the first GaN layer 104 by etching even when the thickness of the Ta layer 103 was changed in this manner.

FIG. 15 diagrammatically shows that a Ta2O5 region formed in the Ta layer 103 varies depending on the thickness of the Ta layer 103. FIG. 15(A) is a diagram showing a Ta2O5 film converted from a 5 nm thick Ta layer 103 and FIG. 15(B) is a diagram showing a Ta2O5 film converted from a surface of a 100 nm thick Ta layer. After depositing the Ta layer 103 on the surface of the first GaN layer 102 using an electron beam (EB) deposition apparatus, the Ta layer 103 was transferred to an MOCVD apparatus while being exposed to air. During the transfer of the Ta layer 103, the Ta layer 103 was converted into Ta2O5 by reaction with oxygen. As a result, when the Ta layer 103 was deposited to a thickness of 5 nm as shown in FIG. 15(A), the overall Ta layer 103 was converted into Ta2O5, and when the 100 nm thick Ta layer 103 was deposited as shown in FIG. 15(B), the surface of the Ta layer 103 was converted into Ta2O5. In other words, when Ta contacts air at room temperature, Ta2O5 is formed. FIG. 15(A) diagrammatically shows an example of lateral growth of a 5 nm thick Ta layer on a GaN layer. Further, FIG. 16 shows an example of lateral growth of a 10 nm thick Ta2O5 film on a substrate. In both examples, the growth was progressed without etching of the GaN layer under the Ta layer. In other words, when a substrate having a 5 nm thick Ta layer formed thereon is transferred to the MOCVD apparatus while being exposed to air, a 5 nm thick Ta2O5 film was formed on the substrate in FIG. 15(A). The Ta2O5 film is a very good mask which grows laterally. On the other hand, when the 100 nm thick Ta layer was deposited as shown in FIG. 15(B), the result was different. When the Ta layer is deposited by EB deposition, a raw material of Ta is positioned in air and a thin oxide film is thus formed on the Ta layer. As Ta is further deposited, it is converted initially into Ta2O5, but is gradually settled down to allow deposition of Ta. The Ta2O5 film has a thickness of 5 nm or less on the GaN layer and contains a portion composed of Ta. An upper layer of the Ta2O5 film is composed of Ta. Further, as the substrate having the Ta layer formed thereon is transferred to the MOCVD apparatus while being exposed to air, a thin Ta2O5 film is formed on the Ta layer. As a result, the surface of the Ta layer is enveloped in the thin Ta2O5 film. In this Ta layer, the Ta2O5 film on the GaN layer is partially mixed with Ta. This result is diagrammatically shown in FIG. 15(B). Although N of the GaN layer and Ta of the Ta layer are coupled to form TaN, Ga is still used as the raw material, since Ga is the same as Ga deposited during vapor deposition.

In the first, second, third, and fourth examples, a Ta₂O₅ region formed by oxidation of the Ta layer 103 is laterally grown with respect to the first GaN layer 102 and serves as a very good etching mask. As a result, in the second example, as shown in FIG. 12, it was ascertained that the Ta₂O₅ region was not formed at the opposite ends of the 30 nm thick Ta layer 103, and the formation of the cavity 102 a was progressed from portions of the first GaN layer 102 under the opposite ends of the Ta layer 103. In both the third and fourth examples, in which the Ta layers 103 were formed to a thickness of 50 nm and a thickness of 100 nm, respectively, the formation of the cavity 102 a was progressed as in the second example, since the Ta₂O₅ region was formed on the surface of the Ta layer to act as the etching mask with respect to the first GaN layer 102.

Accordingly, as in the first, second, third, and fourth examples, a thickness of the Ta layer 103 may be in the range of 20˜100 nm in order to permit formation of the Ta₂O₅ region, which acts as the etching mask. Further, in FIG. 16(A), which shows an example of a 5 nm thick Ta mask formed on the first GaN layer 102, the cavity 102 a is not formed under the Ta mask. Further, in FIG. 16(B), which shows an example of forming only the Ta₂O₅ mask, it is ascertained that the Ta₂O₅ mask can be formed on the GaN layer and InGaAlN layer, for example. Thus, since the Ta₂O₅ mask is formed regardless of the thickness of the Ta layer 103, it is possible to progress the formation of the cavity 102 a in the first GaN layer 102 under the Ta₂O₅ mask.

In the first exemplary embodiment, the Ta layer 103 is formed in the shape of stripes on the first GaN layer 102, and the cavity 102 a is formed at a portion of the first GaN layer 102 under the Ta layer 103 by using the Ta layer 103 as an etching mask. In the second exemplary embodiment, Ti and Cr are used as materials for the etching mask.

FIG. 17 is a flow diagram of a method of manufacturing a semiconductor substrate 300 in accordance with the second exemplary embodiment. In FIG. 17, (A) is a sectional view of a process of forming a first GaN layer, (B) is a sectional view of a process of forming a Ti (or Cr) layer, (C) is a sectional view of a process of forming a second GaN layer and a cavity, (D) is a sectional view of the semiconductor substrate after forming the second GaN layer, (E) is a sectional view of the semiconductor substrate from which a sapphire substrate is separated, and (F) is a sectional view of a finished GaN substrate. In the description of the second exemplary embodiment of FIG. 17, the same components of the semiconductor substrate 100 as those of the first exemplary embodiment will be denoted by the same reference numerals as those shown in FIG. 1.

Referring to FIG. 17(A), reference numeral 101 indicates a sapphire (Al₂O₃) substrate. First, a first GaN layer 102 having a thickness of about 2 μm is formed on the sapphire substrate 101. This thickness of the first GaN layer 102 is provided as an example.

Next, referring to FIG. 17(B), a Ti layer (metallic material layer) 301 having a thickness of about 50 nm is formed in a shape of stripes, which have a width of 5 μm and are separated a distance of 5 μm from each other, on the first GaN layer 102 by electron beam (EB) deposition and lift-off. The shape, thickness, width, and distance of the Ti layer 301 are provided as one example.

Next, referring to FIG. 17(C), a second GaN layer 104 is formed on the first GaN layer 102 and the Ti layer 301 by metal organic chemical vapor deposition (MOCVD). The first GaN layer 102 and the second GaN layer 104 may include different semiconductor material such as AlGaN, InGaN, or AlInGaN. FIG. 17(C) shows the second GaN layer 104 during formation thereof. In the present exemplary embodiment, N in the first GaN layer 102 combines with Ti to form TiN, which acts as foreign matter and rises towards a vapor having a higher density of N. The TiN becomes unstable at 900° C. or more, and holes 301 a are deepened to form cavities 102 a depending on the degree of instability. Here, although N in the first GaN layer 102 becomes TiN, Ga remains in the first GaN layer 102. Since this Ga remaining in the first GaN layer 102 is the same as Ga deposited during the vapor deposition, it is used as the raw material.

Next, referring to FIG. 17(D), once the formation of the second GaN layer 104 is completed, the semiconductor substrate 300 is formed. While the second GaN layer 104 is formed by MOCVD, a portion of the first GaN layer 102 under the Ti layer 301 is removed by etching and a formation region of the cavity 102 a is extended substantially to the sapphire substrate 101. Further, since the growth of the first GaN layer 102 is progressed together with the growth of the second GaN layer 104, the surface of the substrate is flattened as shown in FIG. 17. Thus, it is possible to omit the process of flattening the substrate surface in the semiconductor substrate 300 of this embodiment.

Next, FIGS. 17(E) and 17(F) show a process of separating the sapphire substrate 101 and a process of polishing the first GaN layer 102 separated from the sapphire substrate 101, which are the same as those described with reference to FIGS. 1(E) and 1(F). A detailed description thereof will be omitted herein.

As such, when the semiconductor substrate 300 including the GaN layer is formed by MOCVD, the first GaN layer 102 can be easily separated from the sapphire substrate 101 using the cavity 102 a, so that the separated GaN layer can be used as the GaN substrate 300. Therefore, the GaN substrate 300 may be manufactured at lower costs than the conventional GaN substrate. A detailed example of the manufacturing method of the semiconductor substrate 300 shown in FIG. 17 will be described hereinafter in a first example of the second exemplary embodiment (the fifth example), in which Cr is used as a material for the etching mask.

A detailed example of the manufacturing method of the semiconductor substrate 300 having the Ti layer 301 formed thereon will be described hereinafter. In the fifth example, the process of forming the second GaN layer 104 using an MOCVD apparatus will be described. In this example, crystal growth was performed at a heating temperature of 1045° C. for 50 minutes while supplying TMG as a raw gas at a flux of 80 μmol/min. Further, in the fifth example, a Ti layer 301 having a thickness of 50 nm was formed in a shape of stripes on the first GaN layer 102.

In FIG. 18(A), the semiconductor substrate 300 with the second GaN layer 104 formed thereon under these conditions is shown. FIG. 18(A) is a SEM micrograph of a side section of a portion of the semiconductor substrate 300. As shown in FIG. 18(A), the cavity 102 a is formed at a portion of the first GaN layer 102 under the Ti layer 301. Further, in the fifth example, it was observed that holes 301 a were formed in the Ti layer 301 during the formation of the second GaN layer 104 (see FIG. 17(C) and FIG. 17(D)).

As such, for the semiconductor substrate 300 of the fifth example, the conditions for forming the second GaN layer 104 using the MOCVD apparatus were adjusted, thereby enabling the cavity 102 a to be formed in the first GaN layer 102 using the Ti layer 301 by etching. Thus, when the second GaN layer 104 was formed as illustrated in the second exemplary embodiment, it was possible to form the cavity 102 a in the first GaN layer 102 by etching during growth of the first GaN layer 102. In other words, when the Ti layer 301 as a metallic material layer was partially formed on the first GaN layer 102, it was possible to form the cavity 102 a in the first GaN layer 102. The Ti metallic material layer may be used for etching the first GaN layer 102 as discussed above.

In addition, the MOCVD conditions for the fifth example are provided as an example, and thus, may be set to allow the growth of the first GaN layer and the formation of the cavity 102 a to be simultaneously progressed. Here, since the growth rate of the first GaN layer 102 is slower than that of the second GaN layer 104, the MOCVD conditions were adjusted in consideration of the growth rate of the first GaN layer 102 in the fifth example.

Further, in second exemplary embodiment, the holes 301 a were formed in the Ti layer 301 during the process of growing the second GaN layer 104, but, for example, the Ti layer 301 may be formed using a mask which is previously formed with a hole. Further, the shape of the Ti layer 301 is not limited to the aforementioned stripe shape, and may be changed depending on a device structure to be formed on the semiconductor substrate 300. An example of a device formed using the semiconductor substrate 300 will be described below.

Further, the semiconductor substrate 300 of the second exemplary embodiment may be reused as a substrate 101 forming a GaN layer having the aforementioned cavity by separating the GaN substrate and a surface of the sapphire substrate 101 on which a new GaN substrate is formed may be flattened by RIE or the like. Hence, manufacturing costs of the GaN substrate can be further reduced.

A second comparative example relating to the fifth example will be described hereinafter. In the second comparative example, the process of forming the second GaN layer 104 of the semiconductor substrate 300 under different MOCVD conditions by changing the thickness of the Ti layer 301 will be described.

In the second comparative example, crystal growth was performed at a heating temperature of 1120° C. for 5 hours while supplying TMG as a raw gas at a flux of 20 μmol/min. FIG. 18(B) shows the semiconductor substrate 300 with the second GaN layer 104 formed thereon under these conditions. In FIG. 18(B), the Ti layer 301 has a thickness of 10 nm. In this case, the cavity 102 a is not formed in the first GaN layer 102 under the Ti layer 301.

Accordingly, it is ascertained that when using Ti as a material for the etching mask, a preferred thickness of the Ti layer 301 permitting the cavity 102 a to be formed in the first GaN layer 102 is 50 nm or more, and a preferred flux X of TMG is lower than 80 μmol/min (that is, X<80 μmol/min).

A detailed example of the manufacturing method of the semiconductor substrate 300 having the Cr layer formed thereon will be described hereinafter. In a first condition of a second example of the second exemplary embodiment (a sixth example), the process of forming the second GaN layer 104 using the MOCVD apparatus will be described. In the first condition, crystal growth was performed at a heating temperature of 1060° C. for 40 minutes while supplying TMG as a raw gas at a flux of 80 μmol/min. Further, in the first condition of the sixth example, a 23 nm thick Cr layer was formed in a shape of stripes on the first GaN layer 102.

In FIG. 19(A), the semiconductor substrate 300 with the second GaN layer 104 formed thereon under the first condition is shown. FIG. 19(A) is a SEM micrograph of a side section of a portion of the semiconductor substrate 300. As shown in this figure, the cavity 102 a formed at a portion of the first GaN layer 102 under the Cr layer.

In a second condition of the sixth example, crystal growth was performed at a heating temperature of 1045° C. for 40 minutes while supplying TMG as a raw gas at a flux of 80 μmol/min. Further, in the second condition of the sixth example, a 50 nm thick Cr layer was formed in a shape of stripes on the first GaN layer 102.

In FIG. 19(B), the semiconductor substrate 300 with the second GaN layer 104 formed thereon under the second condition is shown. FIG. 19(B) is a SEM micrograph of a side section of a portion of the semiconductor substrate 300. As shown in FIG. 19(B), the cavity 102 a is formed at a portion of the first GaN layer 102 under the Cr layer.

For the semiconductor substrate 300 of the sixth example, the conditions for forming the second GaN layer 104 using the MOCVD apparatus were adjusted, thereby enabling the cavity 102 a to be formed in the first GaN layer 102 using the Cr layer by etching. Thus, when the second GaN layer 104 was formed as illustrated in second exemplary embodiment, it was possible to form the cavity 102 a in the first GaN layer 102 by etching during growth of the first GaN layer 102. In other words, when the Cr layer as a metallic material layer was partially formed on the first GaN layer 102, it was possible to form the cavity 102 a in the first GaN layer 102. The Cr metallic material layer may be used for etching the first GaN layer 102 as discussed above.

Further, the MOCVD conditions for the sixth example are provided as examples, and thus, may be set to allow the growth of the first GaN layer and the formation of the cavity 102 a to be simultaneously progressed. Here, since the growth rate of the first GaN layer 102 is slower than that of the second GaN layer 104, the MOCVD conditions were adjusted in consideration of the growth rate of the first GaN layer 102 in the sixth example.

A third comparative example will be described hereinafter. In the third comparative example, the semiconductor substrate is formed by forming a metallic material layer other than the Ti layer and the Cr layer, which are formed in the fifth and sixth examples, respectively.

FIG. 20 is a SEM micrograph of a side section of a semiconductor substrate using a tungsten (W) layer as the metallic material layer. For this semiconductor substrate, a 17 nm thick W layer was formed as the metallic material layer in a stripe pattern on the first GaN layer, and the second GaN layer was formed by crystal growth at a temperature of 1045° C. for 40 minutes while supplying TMG as a raw gas at a flux of 80 μmol/min using the MOCVD apparatus. In this case, the cavity was not formed in the first GaN layer under the W layer.

FIG. 21 is a SEM micrograph of a side section of a semiconductor substrate using a platinum (Pt) layer as the metallic material layer. For this semiconductor substrate, an 8 nm thick Pt layer was formed as the metallic material layer in a stripe pattern on the first GaN layer, and the second GaN layer was formed by crystal growth at a heating temperature of 1120° C. for 40 minutes while supplying TMG at a flux of 80 μmol/min using the MOCVD apparatus. In this case, the cavity was not formed in the first GaN layer under the Pt layer.

FIG. 22 is a SEM micrograph of a side section of a semiconductor substrate using a nickel (Ni) layer as the metallic material layer. For this semiconductor substrate, a 12 nm thick Ni layer was formed as the metallic material layer in a stripe pattern on the first GaN layer, and the second GaN layer was formed by crystal growth at a heating temperature of 1045° C. for 40 minutes while supplying TMG at a flux of 80 μmol/min using the MOCVD apparatus. In this case, the cavity was not formed in the first GaN layer under the Ni layer.

FIG. 23 is a SEM micrograph of a side section of a semiconductor substrate using a molybdenum (Mo) layer as the metallic material layer. For this semiconductor substrate, a 30 nm thick Mo layer was formed as the metallic material layer in a stripe pattern on the first GaN layer, and the second GaN layer was formed by crystal growth at a heating temperature of 1045° C. for 40 minutes while supplying TMG at a flux of 80 μmol/min using the MOCVD apparatus. In this case, the cavity was not formed in the first GaN layer under the Mo layer.

As such, when using the W layer, Pt layer, Ni layer, and Mo layer as the metallic material layer, the cavity was not formed in the first GaN layer 102, and thus, the semiconductor substrate enabling the first GaN layer 102 to be separated from the sapphire substrate using the cavity was not manufactured.

Further, in the semiconductor substrates 100 and 300 of the first and second embodiments, the Ta layer 103, the Ti layer 301, and the Cr layer are formed as the metallic material layer in the stripe pattern on the first GaN layer 102, but a material used for an underlayer of the metallic material layer is not limited to GaN. That is, any material comprising N, which reacts with the metallic material layer, may be used. For example, InGaAlN may be used as the material for the underlayer of the metallic material layer.

In the third exemplary embodiment, when forming the second GaN layer, a portion of the second GaN layer is initially formed on the first GaN layer and the Ta layer, and an additional second GaN layer is formed by ultrasound cleaning the semiconductor substrate to remove the Ta layer.

FIG. 24A is a flow diagram of a method of manufacturing a semiconductor substrate 400 in accordance with the third exemplary embodiment. In FIG. 24A, (A) is a sectional view of a process of forming a first GaN layer, (B) is a sectional view of a process of forming a Ta layer, (C) is a sectional view of a process of forming a second GaN layer and a cavity, (D) is a sectional view of a finished semiconductor substrate, (E) is a sectional view of a process of separating a sapphire substrate, and (F) is a sectional view of a finished GaN substrate.

Referring to FIG. 24A(A), reference numeral 401 indicates a sapphire (Al₂O₃) substrate. First, a first GaN layer 402 having a thickness of about 2 μm is formed on the sapphire substrate 401. This thickness of the first GaN layer 402 is provided as an example.

Next, referring to FIG. 24A(B), a Ta layer (metallic material layer) 403 having a thickness of about 5 μm is formed in a shape of stripes, which have a width of 5 μm and are separated a distance of 4 μm from each other, on the first GaN layer 402 by electron beam (EB) deposition and lift-off. The shape, thickness, width, and distance of the Ta layer 403 are provided as one example.

Referring to FIG. 24A(C), a portion of a second GaN layer 404 is formed on the first GaN layer 402 and the Ta layer 403. The first GaN layer 402 and the second GaN layer 404 may include different semiconductor material, such as AlGaN, InGaN, or AlInGaN. In order to form this second GaN layer 404, a semiconductor substrate 400 having the Ta layer 403 formed on the first GaN layer 402 in 24A(B) is placed in an MOCVD apparatus (not shown), and is held at 1000° C. for 20 minutes at a pressure of 500 Torr in the MOCVD apparatus while supplying NH₃ gas at a flux of 0.4 mol/min thereto. FIG. 26(A) is a SEM micrograph of a surface of the semiconductor substrate 400 having the portion of the second GaN layer 404 formed by this process. FIG. 26(B) is a SEM micrograph of a side section of this semiconductor substrate. In the present exemplary embodiment, the semiconductor substrate 400 has an irregular surface. In this process, although TMG is not supplied as the raw material while supplying the NH₃ gas, the second GaN layer is grown as shown in FIG. 26(B). The reason behind this is that, in the MOCVD apparatus, Ga of the first GaN layer 402 reacts with the NH₃ gas at 1000° C. or more to form GaN, thereby allowing the growth of the second GaN layer 404. Further, TaN becomes unstable at 900° C. or more, and a hole is deepened to form a cavity 402 a depending on the degree of instability. Here, although N in the first GaN layer 402 forms TaN, Ga remains in the first GaN layer 402. Since this Ga remaining in the first GaN layer 402 is the same as Ga deposited during vapor deposition, it is used as the raw material. Further, when forming the portion of the second GaN layer 404, TMG may be used as the raw material instead of the NH₃ gas as in the first exemplary embodiment. For example, the portion of the second GaN layer 404 may be formed by crystal growth at a heating temperature of 1045° C. while supplying TMA at a flux of flux of 20 μmol/min in the MOCVD apparatus.

Next, referring to FIG. 24A(D), the semiconductor substrate 400, which has an irregular surface and on which the portion of the second GaN layer 404 is formed in FIG. 24A(C), is removed from the MOCVD apparatus, and the surface of the semiconductor substrate 400 is then cleaned using pure water for 15 minutes at 45 kHz by an ultrasound washer (not shown). The Ta layer 403 is removed by this ultrasound cleaning. FIG. 27(A) is an optical micrograph of the surface of the semiconductor substrate 400, from which the Ta layer 403 is removed. As shown in FIG. 27(A), when the Ta layer 403 is removed, the sapphire substrate 401 and the first GaN layer 402 remain on the surface of the semiconductor substrate 400. In the present exemplary embodiment, after the Ta layer 403 is removed, the holes 404 a are emptied, allowing the first GaN layer 402 to be seen on the surface of the semiconductor substrate and making the surface of the semiconductor substrate 400 more irregular. Further, the hole (indicated by D in FIG. 27(A)) emptied by the removal of the Ta layer 403 has a width of 4 μm. In the present exemplary embodiment, the semiconductor substrate 400 is cleaned by ultrasound cleaning with pure water. The semiconductor substrate 400 may also be cleaned by ultrasound cleaning with a solution that is capable of dissolving the Ta layer 403 but is incapable of dissolving the first and second GaN layers 402 and 404. The solution may be water, water and hydrochloric acid, water and sulfuric acid, water and acetic acid, water and hydrofluoric acid, water and sodium hydroxide, water and potassium hydroxide (here, the amount of water is in the range of 0˜90%), and the like.

Next, referring to FIG. 24A(E), an additional second GaN layer 404 is formed on the first GaN layer 402 of the semiconductor substrate 400, which has the irregular surface, using the MOCVD apparatus. This additional second GaN layer 404 is formed to a thickness of 4.5 μm by heating at 1040° C. for 1 hour at a pressure of 500 Torr in the MOCVD apparatus while supplying TMG at a flux of flux of 160 μmol/min in the MOCVD apparatus. FIG. 26(B) shows a side section of the semiconductor substrate which has the additional second GaN layer 404 formed by this process. As shown in FIG. 26(B), a cavity is formed at a portion of the first GaN layer 402 under the removed Ta layer 403, and the surface of the second GaN layer 404 becomes flattened. Further, in this process, since the Ta layer is previously removed, the granular materials as described in the first exemplary embodiment are not precipitated on the semiconductor substrate.

Further, in FIG. 24A(C), since the portion of the second GaN layer 404 is formed on the first GaN layer 402, it has no defect. Therefore, an interlayer border is not formed between the portion of the second GaN layer and the additional second GaN layer 404 formed thereon in FIG. 24A(E). Further, the portion of the second GaN layer 404 formed in FIG. 24A(C) may be defined as the second GaN layer, and the additional second GaN layer 404 formed in FIG. 24A(E) may be defined as a third GaN layer 405. FIG. 24B shows this example. In FIG. 24B, the respective processes shown in (A) to (E) are the same as those of FIG. 24A, and descriptions thereof will be omitted herein. FIG. 24B(E) shows a structural difference of the second GaN layer from that shown in FIG. 24A(E). In FIG. 24B(E), a GaN layer formed in the process of FIG. 24B(C) is shown as the second GaN layer 404 and a GaN layer formed in the process of FIG. 24B(E) is shown as the third GaN layer 405 (third semiconductor layer). In FIG. 24B(E), a border between the second GaN layer 404 and the third GaN layer 405 is indicated by a dotted line. As such, the GaN layers formed on the first GaN layer 402 before and after the cleaning process are formed by substantially the same crystal growth method and have the same structure. However, since they are grown using different processes, the GaN layers formed on the first GaN layer 402 before and after the cleaning process may be referred to as the second and third GaN layers 404 and 405.

Further, during the formation of the second GaN layer 404 (or third GaN layer 405), the width of the holes 404 a formed after removal of the Ta layer 403 and the internal pressure of the MOCVD apparatus influence the formation of the cavity in the first GaN layer 402. This will be described hereinafter with reference to FIGS. 28 and 29. In FIGS. 28 and 29, the width of the holes 404 a are indicated by a distance “d” between the first GaN layers 402. FIG. 28(A) is a sectional view showing a grown state of the GaN layer, in which the distance “d” is relatively small, and FIG. 28(B) is a sectional view showing a grown state of the GaN layer, in which the distance “d” is relatively large. FIG. 29(A) is a sectional view showing TMG density in a vapor and a grown state of the GaN layer when the first GaN layers 402 are separated a relatively small distance “d” from each other and the internal pressure “P” of the MOCVD apparatus is relatively low. FIG. 29(B) is a sectional view showing TMG density in a vapor and a grown state of the GaN layer when the first GaN layers 402 are separated a relatively large distance “d” from each other and the internal pressure “P” of the MOCVD apparatus is relatively high. FIG. 29(C) is a sectional view showing TMG density in a vapor and a grown state of the GaN layer when the first GaN layers 402 are separated a relatively small distance “d” from each other and the internal pressure “P” of the MOCVD apparatus is relatively high. FIG. 29(D) is a sectional view showing TMG density in a vapor and a grown state of the GaN layer when the first GaN layers 402 are separated a relatively large distance “d” from each other and the internal pressure “P” of the MOCVD apparatus is relatively low.

First, FIG. 28(A) and FIG. 28(B) will be described. In FIG. 28(A) and FIG. 28(B), when the first GaN layer 402 has a thickness of 4 μm, the distance “d” between the first GaN layer in FIG. 28(A) is less than 4 μm (d<4 μm), and the distance “d” between the first GaN layer in FIG. 28(B) is greater than 10 μm (d>10 μm). Such a distance between the first GaN layers 402 depends on the width of the Ta layer 403. For example, when the width of the Ta layer 403 is set to 4 μm in the process of forming the Ta layer 403, the distance between the first GaN layers 402 becomes less than 4 μm due to the hole 404 a formed in the first GaN layer 402 after the Ta layer 403 is removed by the ultrasound cleaning, as shown in FIG. 28(A). Further, for example, when the width of the Ta layer 403 is set to 10 μm in the process of forming the Ta layer 403, the distance between the first GaN layers 402 becomes greater than 10 μm due to the hole 404 a formed in the first GaN layer 402 after the Ta layer 403 is removed by the ultrasound cleaning, as shown in FIG. 28(B).

Further, in the process of forming the second GaN layer (or third GaN layer 405) of FIG. 24A(E) (or FIG. 24B(E)), a growing process of a regrown GaN layer shown in FIG. 28(A) is different from that shown in FIG. 28(B) due to the internal pressure of the MOCVD apparatus and the distance “d” between the first GaN layers 402. In both growing processes of the regrown GaN layer shown in FIG. 28(A) and FIG. 28(B), when the internal pressure of the MOCVD apparatus was set to 500 Torr, the GaN layer was not joined to the sapphire substrate of FIG. 28(A), but it was joined to the sapphire substrate of FIG. 28(B). On the other hand, when the internal pressure of the MOCVD apparatus was set to a pressure less than 500 Torr, for example, 10˜100 Torr, the GaN layer was not joined to the sapphire substrate in both cases of FIG. 28(A) and FIG. 28(B). In other words, when the MOCVD apparatus is set to have a relatively low internal pressure, the GaN layer is not joined to the sapphire substrate even in the case of a relatively large distance between the first GaN layers. Further, when the MOCVD apparatus is set to have a relatively high internal pressure, the GaN layer is joined to the sapphire substrate even in the case of a relatively small distance between the first GaN layers.

Next, a relationship between a grown state of the regrown GaN layer and the internal pressure of the MOCVD apparatus and the distance “d” between the first GaN layers will be described with reference to FIG. 29. In (A) to (D) of FIG. 29, the term “TMG density in a vapor” means the density (m⁻³) of TMG in a vapor, in which TMG is supplied for growing the regrown GaN layer. “TMG density in a vapor” varies depending on the internal pressure of the MOCVD apparatus. When the pressure is set to a relatively low pressure, for example, 10˜100 Torr in the MOCVD apparatus, the TMG density (m⁻³) in the vapor is lowered to increase a mean free process of TMG together and a migration length (diffusion length) of the TMG in the GaN layer, thereby retarding the growth of the GaN layer. On the other hand, when the pressure is set to a relatively high pressure, for example, 200˜760 Torr in the MOCVD apparatus, the TMG density (m⁻³) in the vapor is increased to reduce the mean free process of TMG and the migration length (diffusion length) of the TMG in the GaN layer, thereby promoting the growth of the GaN layer. Thus, when the first GaN layers are separated at constant intervals “d” from each other, the amount of GaN joined to the sapphire substrate is further lowered by setting the internal pressure of the MOCVD apparatus to a relatively low value. On the other hand, when a silicon substrate is used instead of the sapphire substrate and the supplied amount of TMG is constant, the amount of GaN joined to the sapphire substrate is not changed and does not depend on the internal pressure of the MOCVD apparatus. This result is related to lattice parameters of the GaN layer and the substrate. Further, the arrows shown in FIG. 29(A) and FIG. 29(B) indicate growth directions of the GaN layer, and show that the regrown GaN layers are vertically grown with respect to surfaces (top surface and inclined surface) of the first GaN layer 402.

In FIG. 29(A), the distance “d” between the first GaN layers 402 is set to a relatively small value (d<4 μm) and the internal pressure “P” of the MOCVD apparatus is set to a relatively low value, for example, 10˜100 Torr. In this case, the TMG density (m⁻³) in the vapor is lowered to increase the migration length (diffusion length) of the TMG in the GaN layer, thereby retarding the growth of the GaN layer. As a result, the GaN layer is not joined to the sapphire substrate shown in FIG. 29(A). In FIG. 29(B), the distance “d” between the first GaN layers 402 is set to a relatively large value (d>10 μm) and the internal pressure “P” of the MOCVD apparatus is set to a relatively high value, for example, 200˜600 Torr. In the present exemplary embodiment, the TMG density (m⁻³) in the vapor is increased to shorten the migration length (diffusion length) of the TMG in the GaN layer, thereby promoting the growth of the GaN layer. As a result, the GaN layer is joined to the sapphire substrate shown in FIG. 29(B).

Under the conditions of FIG. 29(A) (that is, the relatively small distance “d” between the first GaN layers and the relatively low internal pressure “P” of the MOCVD apparatus), since joining GaN to the sapphire substrate may be difficult, the hole 404 a formed after the removal of the Ta layer 403 is not filled with the regrown GaN layer through growth of the regrown GaN layer, so that the cavity 402 a formed in the first GaN layer 402 remains. Further, under the conditions of FIG. 29(B) (that is, the relatively large distance “d” between the first GaN layers and the relatively high internal pressure “P” of the MOCVD apparatus), since GaN may be easily joined to the sapphire substrate, the hole 404 a formed after the removal of the Ta layer 403 is filled with the regrown GaN layer through growth of the regrown GaN layer, so that the cavity 402 a formed in the first GaN layer 402 does not remain.

In FIG. 29(C), the distance “d” between the first GaN layers 402 is set to a relatively small value (d<4 μm) and the internal pressure “P” of the MOCVD apparatus is set to a relatively high value, for example, 200˜600 Torr. In this case, the TMG density (m⁻³) in the vapor is increased to shorten the migration length (diffusion length) of the TMG in the GaN layer, thereby promoting the growth of the GaN layer. As a result, the GaN layer is joined to the sapphire substrate shown in FIG. 29(B). In the present exemplary embodiment, the amount of GaN joined to the sapphire substrate is less than the amount of GaN joined to the sapphire substrate shown in FIG. 29(B). That is, when the internal pressure of the MOCVD apparatus is set to be relatively high, a relatively small distance “d” between the first GaN layers 402 makes it difficult for GaN to be joined to the sapphire substrate. In FIG. 29(D), the distance “d” between the first GaN layers 402 is set to a relatively large value (d>10 μm) and the internal pressure “P” of the MOCVD apparatus is set to a relatively low value, for example, 10˜100 Torr. In the present exemplary embodiment, the TMG density (m⁻³) in the vapor is lowered to increase the migration length (diffusion length) of the TMG in the GaN layer, thereby retarding the growth of the GaN layer. As a result, the GaN layer is not joined to the sapphire substrate shown in FIG. 29(A).

Under the conditions of FIG. 29(C) (that is, the relatively small distance “d” between the first GaN layers and the relatively high internal pressure “P” of the MOCVD apparatus), since GaN may be easily joined to the sapphire substrate, the hole 404 a formed after the removal of the Ta layer 403 is filled with the regrown GaN layer through growth of the regrown GaN layer. However, since the amount of GaN joined to the sapphire substrate is less than that in the case of the relatively large distance “d” between the first GaN layers, the cavity 402 a formed in the first GaN layer 402 is not completely filled therewith. Further, under the conditions of FIG. 29(D) (that is, the relatively large distance “d” between the first GaN layers and the relatively low internal pressure “P” of the MOCVD apparatus), since joining GaN to the sapphire substrate may be difficult, the hole 404 a formed after the removal of the Ta layer 403 is not filled with the regrown GaN layer through growth of the regrown GaN layer, so that the cavity 402 a formed in the first GaN layer 402 remains.

As such, it is ascertained that the cavity 402 may remain or not remain in the first GaN layer 403 depending on the growth conditions of GaN, that is, the internal pressure of the MOCVD apparatus and the distance “d” between the first GaN layers 402, as shown in (A) to (D) of FIG. 29. Accordingly, it is possible to allow the cavity 402 a to remain in the first GaN layer 402 by adjusting the growth conditions of the second GaN layer 404 (or third GaN layer 405) to set a proper distance “d” between the first GaN layers 402 and a proper internal pressure of the MOCVD apparatus.

Next, referring to FIG. 25A(A), the sapphire substrate 401 is separated. Then, referring to FIG. 25A(B), the GaN substrate 400 may be obtained by polishing the first GaN layer 402, from which the sapphire substrate is removed. The GaN substrate 400 may be used as a semiconductor substrate for manufacturing a device by attaching a silicon-based substrate such as Si or SiC to an upper side of the GaN substrate 400 and flattening a lower surface thereof. Furthermore, when the sapphire substrate 401 is separated, the cavity 402 a formed in the first GaN layer 102 may be used. Separation of the sapphire substrate 401 may be performed by, for example, a laser lift-off or polishing process. It should be understood that the method of separating the sapphire substrate 101 is not limited to a specific one in this embodiment. Further, in FIG. 25B, (A) shows a process of separating the sapphire substrate 401 from the semiconductor substrate 400 shown in FIG. 24B(E), and (B) shows a process of polishing the first GaN layer 402, from which the sapphire substrate is separated. In (A) and (B) of FIG. 25B, the border between the second GaN layer 404 and the third GaN layer 405 is shown by a dotted line.

As such, in the third exemplary embodiment, when forming the second GaN layer 404 (or third GaN layer 405), a portion of the second GaN layer 404 (or the second GaN layer 404) is first formed by annealing the semiconductor substrate 400 while adjusting the internal pressure of the MOCVD apparatus to be constant by supplying NH₃ gas thereto. Then, the semiconductor substrate 400 is removed from the MOCVD apparatus to remove the Ta layer 403 by ultrasound cleaning and is then returned back to the MOCVD apparatus. Then, while adjusting the internal pressure of the MOCVD by supplying TMG to the semiconductor substrate therein, an additional second GaN layer 404 (or third GaN layer 405) is formed, thereby allowing the cavity 402 a to be formed in the first GaN layer 402 using a hole, which is formed by removal of the Ta layer 403. Thus, when forming the second GaN layer 404 (or third GaN layer 405) in the third exemplary embodiment, it is possible to form the cavity 402 a in the first GaN layer 402 using the hole formed after the removal of the Ta layer by ultrasound cleaning. In other words, the cavity 402 a may be formed in the first GaN layer 402 by forming the metallic material layer which permits the formation of the hole at a portion on the first GaN layer 402 as described above. Further, in the semiconductor substrate 400 of the third exemplary embodiment, since the Ta layer 403 is removed by the ultrasound cleaning before the second GaN layer 404 is formed, it is possible to form the second GaN layer 404 having a flat surface without forming a granular material on the surface thereof.

In addition, the MOCVD conditions of the third exemplary embodiment are provided as an example, and thus, may be set to allow the second GaN layer 404 (or third GaN layer 405) and the cavity 402 a to be simultaneously formed. Here, since the formation of the cavity 402 a depends on the width of the Ta layer 403 and the internal pressure of the MOCVD apparatus during the growth of the second GaN layer 404 (or third GaN layer 405), the width of the Ta layer 403 and the internal pressure of the MOCVD apparatus are adjusted in the third exemplary embodiment.

Further, in the third exemplary embodiment, the shape of the Ta layer 403 is not limited to the aforementioned stripe shape, and may be changed depending on a device structure to be formed on the semiconductor substrate 400. An example of a device formed using the semiconductor substrate 400 will be described below.

Further, the semiconductor substrate 400 of the third exemplary embodiment may be reused as a substrate 401 forming a GaN layer having the aforementioned cavity by separating the GaN substrate and a surface of the sapphire substrate 401 on which a new GaN substrate is formed may be flattened by RIE or the like. Hence, manufacturing costs of the GaN substrate can be further reduced.

In a fourth exemplary embodiment, a light emitting diode (LED) array formed on the semiconductor substrate 100 of the first exemplary embodiment, the semiconductor substrate 300 of the second exemplary embodiment or the semiconductor substrate 400 of the third exemplary embodiment, will be described with reference to FIG. 11.

FIG. 11 is a sectional view of an LED array in accordance with the fourth exemplary embodiment. In FIG. 11, the semiconductor substrate 100 is applied.

Referring to FIG. 11, LEDs 200 are separated from each other on the semiconductor substrate 100. Each LED 200 includes a lower semiconductor layer 201 composed of a first compound semiconductor layer, an active layer 202, and an upper semiconductor layer 203 composed of a second compound semiconductor layer. The lower semiconductor layer 201 and the upper semiconductor layer 203 may comprise the same class as the first GaN layer 102 and the second GaN layer 104. The active layer 202 may have a single or multi-quantum well structure having a barrier layer, and may be formed of a material and composition selected depending on a desired light emitting field. For example, the active layer 202 may be formed of a gallium nitride-based compound semiconductor. The upper and lower semiconductor layers 201 and 203 may be a gallium nitride-based compound semiconductor having a greater band gap than that of the active layer 202.

In the present exemplary embodiment, the lower semiconductor layer 201 on the semiconductor substrate 100 is formed on the second GaN layer 104. Thus, it is possible to reduce manufacturing costs by manufacturing the LEDs 200 using the semiconductor substrate 100.

The upper semiconductor layer 203 is located above a portion of the lower semiconductor layer 201, and the active layer 202 is interposed between the upper semiconductor layer 203 and the lower semiconductor layer 201. Further, an upper electrode layer 204 may be formed on the upper semiconductor layer 203. The upper electrode layer 204 may be a transparent electrode layer formed of, for example, indium tin oxide (ITO), Ni/Au, and the like.

Further, an upper electrode pad 205 is formed on the upper electrode layer 204 and a lower electrode 207 is formed on an exposed region of the lower semiconductor layer 201.

After the LEDs 200 are formed on the single semiconductor substrate 100 in this manner, the LEDs 200 are divided into individual LEDs 200 by cutting a portion of the semiconductor substrate 100 between the LEDs 200. In the LED of this embodiment, the upper electrode 205 and the lower electrode pad 207 are laterally arranged, but an LED may be manufactured to have vertically arranged electrodes. In other words, a vertical type LED may be manufactured by separating the sapphire substrate 101 using the cavity 102 a of the semiconductor substrate 100, flattening the separated surface of the first GaN layer 102 by RIE or the like, and forming an upper electrode pad 205 and a lower electrode pad 207.

As such, it is possible to reduce manufacturing costs of the LEDs by manufacturing the LEDs 200 using the semiconductor substrate 100 or 300. Further, when forming the LEDs 200 on the second GaN layer 104, it is possible to construct an LED array with improved light emitting efficiency and high brightness by forming the compound semiconductors such that the second GaN layer 104 and the lower semiconductor layer 201 have different indices of refraction from each other. Further, when a laser diode is formed using the GaN substrate 100 or 300, from which the sapphire substrate 101 is separated, it is possible to achieve an improvement in heat dissipation properties together with long lifetime of the laser diode, since the laser diode is formed on the GaN layer 104, which exhibits better thermal conductivity than the sapphire substrate 101.

In the fourth exemplary embodiment, the LEDs 200 are formed on the second GaN layer of the semiconductor substrate 100 or 300. Alternatively, the LEDs 200 may be formed in the same manner using the GaN substrate which is separated from the sapphire substrate 101. In addition, a semiconductor device, such as an FET and the like, may be formed by attaching a silicon-based substrate, such as Si or SiC, as an indication material, to a separated surface of the GaN substrate, which is separated from the sapphire substrate 101, and polishing the separated surface of the GaN substrate by RIE or the like. In this case, a high-current device can be manufactured.

Therefore, the semiconductor substrate 100 or 300 is used to manufacture semiconductor devices such as LEDs or laser diodes, thereby facilitating manufacture of high performance semiconductor devices at low cost without using an expensive GaN substrate.

Further, in the first, second, and third exemplary embodiments, the Ta layer, Ti layer and Cr layers are formed as the metallic material layer. However, any metal alloy, alloys of metals and semiconductors, or any metallic material capable of providing an etching phenomenon to the first GaN layer may also be used, such as those discussed in Hasegawa and Haino.

As apparent from the above description, according to the exemplary embodiments, it is possible to provide a method of manufacturing a flat and easily separable GaN substrate on a heterogeneous substrate at low cost. It is also possible to realize performance improvement and long operational lifespan of semiconductor devices, such as LEDs or laser diodes, which are manufactured using the GaN substrate.

It will be apparent to those skilled in the art that various modifications and variation can be made in the present invention without departing from the spirit or scope of the invention. Thus, it is intended that the present invention cover the modifications and variations of this invention provided they come within the scope of the appended claims and their equivalents. 

What is claimed is:
 1. A method of manufacturing a semiconductor substrate, the method comprising: forming a first semiconductor layer on a substrate; forming a metallic material layer on the first semiconductor layer; forming a first portion of a second semiconductor layer on the first semiconductor layer and the metallic material layer; removing the metallic material layer under the first portion of the second semiconductor layer by dipping the substrate in a solution; forming a second portion of the second semiconductor layer on the first portion of the second semiconductor layer; and forming a cavity in a portion of the first semiconductor layer located under where the metallic material layer was removed.
 2. The method of claim 1, further comprising: forming a third semiconductor layer on the second semiconductor layer.
 3. The method of claim 1, wherein the metallic material layer is removed by ultrasound cleaning a portion of the substrate on which the second semiconductor layer is formed.
 4. The method of claim 2, wherein the metallic material layer is removed by ultrasound cleaning a portion of the substrate on which the second semiconductor layer is formed.
 5. The method of claim 1, wherein the solution dissolves the metallic material layer and does not dissolve the first semiconductor layer or the second semiconductor layer.
 6. The method of claim 1, wherein the solution is one selected from water, water and hydrochloric acid, water and sulfuric acid, water and acetic acid, water and hydrofluoric acid, water and sodium hydroxide, and water and potassium hydroxide.
 7. The method of claim 1, wherein the metallic material layer is removed by ultrasound cleaning a portion of the substrate on which the second semiconductor layer is formed, using water.
 8. The method of claim 2, wherein the metallic material layer is removed by ultrasound cleaning a portion of the substrate on which the second semiconductor layer is formed, using water.
 9. A method of manufacturing a semiconductor substrate, the method comprising: forming a first semiconductor layer on a substrate; forming a metallic material layer on the first semiconductor layer; forming a second semiconductor layer on the first semiconductor layer and the metallic material layer; and forming a cavity in a portion of the first semiconductor layer under the metallic material layer.
 10. The method of claim 9, wherein the first semiconductor layer comprises nitrogen.
 11. The method of claim 9, wherein the substrate comprises a sapphire substrate or a silicon-based substrate.
 12. The method of claim 9, wherein the semiconductor substrate is formed by separating the substrate from the first semiconductor layer and the second semiconductor layer using the cavity formed in the first semiconductor layer.
 13. The method of claim 12, wherein a laser lift-off process is used to separate the substrate.
 14. The method of claim 12, wherein a polishing process is used to separate the substrate.
 15. The method of claim 1, wherein the semiconductor substrate is formed by separating the substrate from the first semiconductor layer and the second semiconductor layer using the cavity formed in the first semiconductor layer. 